热疲劳,thermal fatigue
1)thermal fatigue热疲劳
1.Study of failure mode and failure mechanisms onthermal fatigue of plasma sprayed thermal barrier coatings;等离子涂层热疲劳失效模式及失效机理研究
2.Changes of morphology and composition of carbides in H13 steel afterthermal fatigue;H13钢热疲劳后碳化物形态和组分的变化
3.Effect of heat treatment conditions on thethermal fatigue properties of WC/steel composites;热处理条件对WC/钢复合材料热疲劳性能的影响
英文短句/例句
1.The Behaviors of γ-TiAl Alloy under Thermal Fatigue and Dead-load Thermo-mechanical Fatigue;γ-TiAl合金的热疲劳与静载热机械疲劳行为
2.The Effect of Heat Treatment Technics on the Thermal Fatigue Property of 3Cr2W8V Steel;热处理工艺对3Cr2W8V钢热疲劳性能的影响
3.The Thermal Shock and Fatigue Behaviors of Al_2O_3-TiC Composite Ceramic;Al_2O_3-TiC复合陶瓷的热震和热疲劳行为
4.A CHANGES IN GRAIN SIZE AND SOFTENING MECHANISM OF DIE STEEL DURING THERMAL FATIGUE模具钢热疲劳中晶粒变化及软化机制
5.Thermomechanical Fatigue Properties of Lead-Free Solder Joints;无铅合金钎焊接头热疲劳性能的研究
6.Study of Thermal Fatigue on Al-Cu-Mn-Ti-Ce Alloy;Al-Cu-Mn-Ti-Ce合金热疲劳性能的研究
7.Numerical simulation on thermal fatigue behavior of CuCGA soldered jointsCuCGA器件焊点热疲劳行为数值模拟
8.Research on Thermal Fatigue Property of Coating on Steel Surface钢表面镀覆层热疲劳性能研究的进展
9.A STUDY ON THE METHOD OF MEASURING THE THERMAL-FATIGUE PROPERTY FOR DIE STEELS热作模具钢热疲劳性能测定方法的研究
10.Study on Thermal Fatigue Property of Hot Working Die Treated by Laser Biomimetic Coupling Technique;激光仿生耦合处理热作模具的热疲劳性能研究
11.Thermal Fatigue Research on Hot Work Steel with Biomimetic Coupling Surfaces Processed by Laser;激光仿生耦合热作模具钢热疲劳性能研究
12.Study on the Factor of Affecting Thermal Fatigue Property of Hot Work Steel;热作模具钢的热疲劳性能影响因素的研究
13.High Temperature Oxidation, Hot Corrosion and Thermal Fatigue Behavior of GH4698 Superalloy;GH4698合金的高温氧化、热腐蚀及热疲劳性能的研究
14.Study on the Cold-Hot Deformation and Laser Thermal Fatigue of IN718 and 1100 Aluminum Alloy;IN718和1100铝合金冷热变形及激光热疲劳研究
15.Conduct material Fatigue Testing and Thermal stress test.进行材料疲劳测试和热应力测试。
16.A layer of hot-dipped galvanizing causes a considerable reduction in the fatigue strength.热浸镀锌层引起疲劳强度的显著降低。
17.The consequence is accelerated material fatigue due to overheating.其结果是因过热加速了材料的疲劳。
18.On velocity rhythm in 100m sprint from the perspective of energetics fatigue of nerve center;从中枢热力学疲劳谈100m跑速度节奏
相关短句/例句
heat fatigue热疲劳
1.Investigation of improvement ofheat fatigue resistance of steel 3Cr24Ni7;提高 3Cr24Ni7 钢热疲劳性的研究
2.Three invalid patterns which resulted from the improper heat treatment wereheat fatigue,thermal wear,two invalid patterns appeared concurrence,the invalid patterns were mainly studied,and the solved approaches were put forward.重点研究了由于热处理不当引起的三种失效:热疲劳、热磨损、以及两者失效同时发生,并提出了解决的途径。
3.Theheat fatigue of the coat of supporting steel back of the powder metalurgical friction material and rotator material was studied in this article.研究了粉末冶金摩擦材料及对偶材料支承钢背镀层的热疲劳行为。
3)Hot Fatigue热疲劳
1.The propagation rules of hot fatigue of H13 used for die casting dies were studiedthrough simulating the work conditions of die casting dies.依据模拟压铸铝合金模具的工作条件，研究了压铸模具钢H13的热疲劳裂纹的扩展规律。
4)Creep-Fatigue/Thermal-Fatigue蠕变疲劳/热疲劳
5)cold-hot fatigue冷热疲劳
1.CoCrMoSi coating was deposited on CrZrCu with HVOF,and itscold-hot fatigue and war resistance were studied,analyzed and compared with NiCo plated coating widely applied in metallurgy industry.采用光学显微镜、SEM及EDS等方法,对涂层的冷热疲劳性能和抗磨损性能进行了分析研究,并与当前冶金行业大量使用的电镀NiCo镀层进行对比。
2.Co based alloy coating was deposited on the narrow side CrZrCu plate of the slab continuous caster with HVOF and thecold-hot fatigue was compared with Co-Ni plating coating.结果表明:450℃下进行冷热疲劳试验,Co基合金涂层经过113次后,涂层还保持完好无损,未出现任何缺陷,而电镀镀层只能承受37。
6)thermal fatigue冷热疲劳
1.Microstructure andthermal fatigue mechanical properties of cast cobalt-base su peralloy K640S were investigated during a number of recycles.对铸造钴基高温合金K640S进行10次返回处理,研究了母合金和几种不同返回次数返回料的冷热疲劳性能,并进行了金相观察·结果表明:加热到815℃,然后水冷到25℃,保温5min,冷却5s,循环70次时,7返、10返合金首先出现微裂纹·随着循环次数的增加,返回料比新料疲劳裂纹生长快·循环200次时,无论新料还是返回料裂纹长度都达到2mm·随着返回次数的增加,合金中气体及夹杂物质量分数随之增加,枝晶组织越来越发达
延伸阅读
热疲劳分子式：CAS号：性质：当容器或构件由于其温度的反复变化而引起其金属材料的疲劳现象称为热疲劳。